N Type , InAs( Indium Arsenide ) Substrate , 3”, Dummy Grade

N Type , InAs( Indium Arsenide ) Substrate , 3”, Dummy Grade

PAM-XIAMEN manufactures high purity single crystal Indium arsenide Wafers for optoelectronics applications. Our standard wafer diameters range from 25.4 mm (1 inch) to 100 mm (6 inches) in size; wafers can be produced in various thicknesses and orientations with polished or unpolished sides and can include dopants. PAM-XIAMEN can produce wide range grades: prime grade, mechanical grade,test grade, dummy grade, technical grade, and optical grade. PAM-XIAMEN also offers materials to customer specifications by request, in addition to custom compositions for commercial and research applications and new proprietary technologies.

3" InAs Wafer Specification

What is InAs wafer?

Indium arsenide is a kind of III-V compound semiconductor material composed of indium and arsenic.It is a silver gray solid with a sphalerite crystal structure at room temperature. The lattice constant is 0.6058nm, and the density is 5.66g/cm (solid) and 5.90g/cm (liquid at melting point). The band structure is a direct transition with a band gap (300K) of 0.45ev. the dissociation pressure of as is only 0.033mpa, and the single crystal can be grown from the melt at atmospheric pressure. The commonly used methods are Hb and LEC. InAs is a kind of semiconductor material which is difficult to purify. The residual carrier concentration is higher than l × 10 / cm, the room temperature electron mobility is 3.3 × 10 ^ 3cm / (V · s), and the hole mobility is 460cm / (V · s). The effective segregation coefficient of sulfur in In and As is close to 1, so it is used as n-type dopant to improve the uniformity of longitudinal carrier concentration distribution. For industrial InAs (s) single crystal, n ≥ 1 × 10 / cm3, μ ≤ 2.0 × 10cm / (V · s), EPD ≤ 5 × 10 / cm3.

InAs crystal has high electron mobility and mobility ratio (μ E / μ H = 70), low magneto resistance effect and low resistance temperature coefficient. It is an ideal material for manufacturing Hall devices and magneto resistance devices. The emission wavelength of InAs is 3.34 μ M. in GaAs B, InAsPSb and inasb multiple epitaxial materials with lattice matching can be grown on InAs substrate. Lasers and detectors for optical fiber communication at 2-4 μ M band can be manufactured.

Optical properties of InAs wafer

Refractive index n versus photon energy. Solid curve is theoretical calculation. Points represent experimental data, 300 K.

For 3.75 µm < λ < 33 µm
n = [11.1 + 0.71/(1-6.5·λ-2) + 2.75/(1-2085·λ-2) - 6·10-4·λ2)]1/2,
where λ is the wavelength in µn (300 K)

	Normal incidence reflectivity versus photon energy, 300 K
	Absorption coefficient near the intrinsic absorption edge for n-InAs. T=4.2 K
	Absorption coefficient versus photon energy for different donor concentration, 300 K n (cm-3): 1. 3.6·1016, 2. 6·1017, 3. 3.8·1018.

A ground state Rydberg energy RX1= 3.5 meV

	Absorption coefficient versus photon energy, T = 300 K
	Free carrier absorption versus wavelength at different electron concentrations. T=300 K. no (cm-3): 1. 3.9·1018; 2. 7.8·1017; 3. 2.5·1017; 4. 2.8·1016;

Are You Looking for an InAs substrate?

PAM-XIAMEN is proud to offer indium phosphide substrate for all different kinds of projects. If you are looking for InAs wafers, send us enquiry today to learn more about how we can work with you to get you the InAs wafers you need for your next project. Our group team is looking forward to providing both quality products and excellent service for you!

indium arsenide wafer

3 inch wafer